PG30GF it is a kind of glass fiber reinforced PETG particle (the mass percentage of glass fiber is 30%), which has excellent printabilitywarpage resistance and weatherability, and is specially designed for large-area additive manufacturing (BAAM). PG30GF is an optimal choice for 3D printing and injection molding due to their superior strength and durability. Their resistance to heat, pressure and chemical reaction makes them an excellent choice for a wide range of applications.
Product Details
Overview
PG30GF it is a kind of glass fiber reinforced PETG particle (the mass percentage of glass fiber is 30%), which has excellent printabilitywarpage resistance and weatherability, and is specially designed for large-area additive manufacturing (BAAM). PG30GF is an optimal choice for 3D printing and injection molding due to their superior strength and durability. Their resistance to heat, pressure and chemical reaction makes them an excellent choice for a wide range of applications.
Advantages
Exceptional Printing Precision & Stability
Large-Scale Industrial Capability
Advanced Monitoring & Automation
Quiet, High-Speed Performance
Physical Properties
| Property | Test Method | Value | |||
| Density(g/cm3,21.5°℃) | ASTM D792(1S01183,GB/T 1033) | 1.39 | |||
| Distortion temperature(℃) | DSC,10 C/min | 81 | |||
| Glasstransition temperature(℃) | ISO7518MPa | 77 | |||
| 0.45MPa | 82 | ||||
Mechanical Properties
| Property | Test Method | Value | |||
| Flexural Modulus(MPa)(X-Y) | Modified ASTM D790(ISO 178,GB/T9341) | 6094+1344 | |||
| Flexural Strength(MPa)(X-Y) | Modified ASTM D790(ISO 178,GB/T9341) | 128.1+7.8 | |||
| Impact strength(kJ/m3)(X-Y) | Modified ASTM D256(ISO 179,GB/T 1043) | 21.3+0.92 | |||
| Flexural Modulus(MPa)(Z) | Modified ASTM D790(ISO 178,GB/T9341) | 2701+366 | |||
| Flexural Strength(MPa)(Z) | Modified ASTM D790(ISO 178,GB/T9341) | 46.8+3.3 | |||
| Impact strength(kJ/m3)(Z) | Modified ASTM D256(ISO 179,GB/T 1043) | 5.2+1.3 | |||