PG20FR it is a kind of glass fiber reinforced PETG particle (the mass percentage of glass fiber is 20%), which has excellent printability, warpage resistance, and weatherability, and is specially designed for large-area additive manufacturing (BAAM). PG20FR is an optimal choice for 3D printing and injection molding due to its superior strength and durability. Their resistance to heat, pressure, and chemical reaction makes them an excellent choice for a wide range of applications.
Product Details
Overview
PG20FR (PETG+20%GF) is a flame-retardant engineering plastic reinforced with 20% glass fiber. It combines excellent strength, heat resistance, and dimensional stability with superior flame protection, ensuring safety and reliability in demanding applications such as electrical housings, automotive components, and industrial parts.
Advantages
Exceptional Printing Precision & Stability
Large-Scale Industrial Capability
Advanced Monitoring & Automation
Quiet, High-Speed Performance
Physical Properties
Physical Properties
| Property | Test Method | Value | |||
| Density(g/cm³, 21.5°℃) | ISO 1183-1: 2019 | 1.565 | |||
| Vicat Softening Temperature(°C) | ISO 306: 2022 | 89.8 | |||
| Heat Deflection Temperature (°C) | ISO 75-2: 2013 | 78 | |||
| Melt Mass-Flow Rate (g/10min) | ISO 1133-1: 2022 | 2.28 | |||
Mechanical Properties
| Property | Test Method | Value | |||
| Rockwell Hardness(HRR) | ISO 2039-2:1987 | 112R | |||
| Tensile Strength(MPa) | ISO 527-2:2012 | 82.1 | |||
| Tensile Strain at Break(%) | ISO 527-2:2012 | 2.1 | |||
| Tensile Modulus(MPa) | ISO 527-2:2012 | 7740 | |||
| Flexural Strength(MPa) | ISO 178:2019 | 117 | |||
| Flexural Modulus(MPa) | ISO 178:2019 | 8250 | |||
| Izod Impact Strength(kJ/m² ) | ISO 180:2023 | 5.79 (Complete Break) | |||
| Falling Dart Impact(J) | ASTM D5420-21 | Average Breakthrough Energy < 0.25 | |||