KSPA12BK is a black nylon powder featuring a D50 particle size of approximately 50 microns, showcasing a narrow and uniform distribution. It can be sintered using fiber or carbon dioxide lasers, exhibiting high sphericity and exceptional fluidity. With a reusability rate approaching 100%, the 3D printed parts retain outstanding mechanical properties and a flawless surface finish.

Inquire Now

Download

Product Details

Overview

KSPA12BK is a black nylon powder featuring a D50 particle size of approximately 50 microns, showcasing a narrow and uniform distribution. It can be sintered using fiber or carbon dioxide lasers, exhibiting high sphericity and exceptional fluidity. With a reusability rate approaching 100%, the 3D-printed parts retain outstanding mechanical properties and a flawless surface finish.

Ideal Applications

- Functional structures

- Concept prototypes

- Automotive, aerospace, architectural, and electronic applications

Technical Datasheet

Mechanical property	Value	Unit	Test Standard
Tensile Modulus	1600	Mpa	ISO 527
Tensile Strength	46	Mpa	ISO 527
Strain at break	20	%	ISO 527
Charpy impact strength	38	KJ/㎡	ISO 179
Charpy notched impact strength	7.5	KJ/㎡	ISO 179
Flexural modulus	1400	Mpa	ISO 178
Flexural Strength	50	Mpa	ISO 178
Other properties	Value	Unit	Test Standard
Powder Melting temperature (10℃/min)	187	℃	ISO 11357
Vicat softening temperature (50℃/h50N)	100	℃	ISO 11357
Density (Laser Sintered)	0.94	g/cm³	Own method
Density (Powder)	0.52	g/cm³	Own method
Particle Size (D50)	50	μm	Laser Diffraction

Advantages

Exceptional Printing Precision & Stability
Large-Scale Industrial Capability
Advanced Monitoring & Automation
Quiet, High-Speed Performance

Printing Samples

Application

AutomotiveShoe Molds & Footwear PrototypingMedical & HealthcareSculpture & ArtFurniture & Home ApplianceAerospace & Precision EngineeringArchitectureMolds & Tools