KS608 UV Resin is a commonly used 3D printing material with accuracy and durability. Similar to the plastic properties of ABS, it is used in stereolithography (SLA) 3D printers. KS608 UV Resin can be used in model making and prototyping of automotive, medical, consumer electronics, etc.The parts duability building with KS608 UV Resin is over 6.5months.
TYPICAL FEATURES
-Liquid resin`s medium viscosity, so easy recoating, easy clean parts and machines.
-Improved strength retained, improved dimensions retention of parts in humid condition.
-need minimal part finishing.
-Long shelf life in machine.
TYPICAL BENEFITS
-Need less part finishing time,easier post-curing.
-Buliding accurate and high tough parts with an improved dimensional stability.
-High quality controls for vacuum casting parts.
-Color is more close to the ABS.
-Outstanding machinable SLA material.
Physical Properties – Liquid Material
Appearance | White |
Density | 1.13g/cm3 @ 25 ℃ |
Viscosity | 390 cps @ 26 ℃ |
Dp | 0.141 mm |
Ec | 8.6 mJ/cm2 |
Building layer thickness | 0.1mm |
Mechanical Properties of Post-Cured Material
MEASUREMENT | TEST METHOD | VALUE |
|
| 90-minute UV post-cure |
Hardness, Shore D | ASTM D 2240 | 86 |
Flexural modulus, Mpa | ASTM D 790 | 2,498-2,550 |
Flexural strength, Mpa | ASTM D 790 | 70- 75 |
Tensile modulus, MPa | ASTM D 638 | 2,451-2,565 |
Tensile strength, MPa | ASTM D 638 | 40-56 |
Elongation at break | ASTM D 638 | 11 -17% |
Poisson`s Ratio | ASTM D 638 | 0.38-0.42 |
Impact strength notched Izod, J/m | ASTM D 256 | 30 - 43 |
Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 63 |
Glass transition,Tg，℃ | DMA，E”peak | 75 |
Coefficient of thermal expension, /℃ | TMA(T<Tg) | 92*E-6 |
Density 密度, g/cm3 |
| 1.15 |
Dielectric Constant 60 Hz | ASTM D 150-98 | 4.5 |
Dielectric Constant 1 kHz | ASTM D 150-98 | 3.9 |
Dielectric Constant 1 MHz | ASTM D 150-98 | 3.6 |
Dielectric Strength kV/mm | ASTM D 1549-97a | 14.8 |
UV resin 355nm; SLA resin cost; how much does resin cost; photosensitive resin; 3D printing material