KS408 UV Resin is a precise and durable ABS-like resin for industrial SLA 3D printer. It is an ideal 3D printing material with perfect smoothness and details.
Product Details
KS408 UV Resin is a precision and durable ABS-like lithography resin used in SLA 3D printers. It is a master model for the production of common 3D printing materials, automotive, medical, consumer electronics and other industrial fields, conceptual models, general components. , functional components can be produced.The parts durability building with KS408 is over 6.5months.
TYPICAL FEATURES
-The medium viscosity of the liquid resin makes the re-coating as well as the machine and parts cleaning easier
-Improved strength and dimension retention in humid condition
-Need minimal part finishing
-Long shelf life in machine
TYPICAL BENEFITS
-Need less part finishing time, easier post-curing
-Building accurate and high tough parts with an improved dimensional stability
-High quality controls for vacuum casting parts
-Low shrink and good resistance to yellowing
-Magnificent white color
-Outstanding machinable SLA material
Appearance | White |
Density | 1.13g/cm3 @ 25 ℃ |
Viscosity | 355 cps @ 28 ℃ |
Dp | 0.145 mm |
Ec | 9.3 mJ/cm2 |
Building layer thickness | 0.1mm |
MEASUREMENT | TEST METHOD | VALUE |
90-minute UV post-cure | ||
Hardness , Shore D | ASTM D 2240 | 83 |
Flexural modulus, Mpa | ASTM D 790 | 2,692-2,775 |
Flexural strength, Mpa | ASTM D 790 | 69- 74 |
Tensile modulus, MPa | ASTM D 638 | 2,189-2,395 |
Tensile strength, MPa | ASTM D 638 | 27-31 |
Elongation at break | ASTM D 638 | 12 -20% |
Impact strength, notched lzod, J/m | ASTM D 256
| 58 - 70
|
Heat deflection temperature, ℃ | ASTM D 648 @66PSI
| 52
|
Glass transition, Tg,℃ | DMA,E”peak | 62 |
Coefficient of thermal expansion, /℃ | TMA(T<Tg) | 97*E-6 |
Density, g/cm3 | 1.16 |
Note: The temperature for JS-UV-2016 resin processing and storage should be lower than 25℃, and the temperature recommended is 18℃ - 25℃.
UV resin 355nm; SLA resin cost; how much does resin cost; photosensitive resin; 3D printing material